產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 密度 | ASTM D1505 | 1.24 | g/cm3; | |
機械性能 | 薄膜厚度 | 經測試 | 25 | μm | |
割線模量 | MD: 25 μm | ASTM D882 | 3450 | μm | |
TD: 25 μm | ASTM D882 | 3790 | μm | ||
抗張強度 | MD: 屈服, 25 μm | ASTM D882 | 103 | μm | |
TD: 屈服, 25 μm | ASTM D882 | 145 | μm | ||
伸長率 | MD: 斷裂, 25 μm | ASTM D882 | 180 | % | |
TD: 斷裂, 25 μm | ASTM D882 | 100 | % | ||
埃爾曼多夫抗撕強度 | MD: 25 μm | ASTM D1922 | 17 | g | |
TD: 25 μm | ASTM D1922 | 14 | g | ||
透氧率 | ASTM D3985 | 550 | cm3;·mm/m2;/atm/24 hr | ||
水氣透過率 | ASTM F1249 | 330 | g·mm/m2;/atm/24 hr | ||
| 熱性能 | 玻璃轉化溫度 | DSC | DSC | 57.8 | ℃ |
熔融溫度 | 160 | ℃ | |||
| 光學性能 | 光澤度 | 20℃, 25.4 μm | ASTM D2457 | 90 | |
| 霧度 | 25.4 μm | ASTM D1003 | 2.1 | % | |